HDPE 9001 Plastic Raw Material Wires and Cables PE Insulation Materials

• Customization: Available
• Feature: Wear-Resistant, Excellent Appearance, High Density
• CAS No.: 9002 - 88 - 4
• Model NO.: 9007
• Formula: (C2h3cl)N
• EINECS: 200 - 831 - 0
• Material: High Density Polyethylene/HDPE
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Color: Oyster White
• Shape: Granular
• Density: 0.950 g/cm3
• Melt Mass Flow Rate: 0.04 G/10min
• Transport Package: PE Plastic Bag
• Specification: 25KG/bag
• Trademark: tai su
• Origin: China Tai Wan
• HS Code: 390120009
• Production Capacity: 500000

Product Description

Industry-Specific Application Notes

• Outdoor Application Priority: Due to its low brittleness temperature and strong ESCR, this product is particularly suitable for outdoor scenarios (e.g., outdoor communication cables, outdoor pipe coatings) where resistance to temperature changes and environmental corrosion is required.

• Processing Adaptability: For high-pressure processing scenarios (e.g., thick-walled cable sheaths), its high-load melt index (8.5 g/10min under 21.6kg) ensures smooth material flow and uniform product formation.

• Safety Compliance: In electrical and communication fields, the material meets common industry safety standards (e.g., insulation, low-temperature resistance) and is compatible with mainstream processing technologies (extrusion, molding) in these industries. |

 

1. Basic Product Info

 

Item	Details
Product Name	High Density Polyethylene (HDPE) - Formosa Plastics (Taiwan) 9007
Typical Applications	Communication equipment, foam, coatings, wires & cables, insulating materials

2. Physical Properties

 

Property	Value	Test Standard	Remarks
Density	~0.949 g/cc (0.0343 lb/in³)	ASTM D1505	Ensures good rigidity and structural stability
Melt Flow Rate (MFR)	0.040 g/10min (2.16kg, 190ºC)	ASTM D1238 (Condition E)	Low flow; suitable for high-strength products
High-Load Melt Index	8.5 g/10min (21.6kg, 190ºC)	ASTM D1238 (Condition F)	References flow under high-pressure processing

3. Mechanical Properties

 

Property	Value	Test Standard	Remarks
Tensile Yield Strength	24.8 MPa (3600 psi)	ASTM D638	Test speed: 2" (50mm)/min; good anti-stretching ability
Elongation at Break	≥ 600%	ASTM D638	Test speed: 2" (50mm)/min; excellent flexibility

4. Thermal Properties

 

Property	Value	Test Standard	Remarks
Brittleness Temperature	≤ -118ºC (≤ -180°F)	ASTM D746	Maintains flexibility in low-temperature environments

5. Environmental Stress Cracking Resistance (ESCR)

 

Test Method	Value	Test Standard	Remarks
NCLS Method (15% Strain)	400 hours	ASTM F2136	Resists cracking under stress and media
10% Igepal® Solution (Condition B)	≥ 500 hours	ASTM D1693	Suitable for long-term use in complex environments